點(diǎn)擊圖片查看大圖
Lanxess Durethan? BKV 30 N1 000000德國(guó)朗盛PA6,30%玻璃纖維,注塑,阻燃;
Information provided by LANXESS.
Lanxess Durethan? BKV 30 N1 000000 Nylon 6, 30% Glass Fiber
Categories:
Polymer; Thermoplastic; Nylon; Nylon 6; Nylon 6, 30% Glass Fiber Filled
Material Notes:
PA 6, 30% glass fiber, injection molding, flame retardant
Key Words:
ISO 1874-PA 6,GFR,14-120,GF30; ISO1043-PA GF FR(22)
Vendors:
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
Add to Folder: My Folder
Physical Properties
Metric
English
Comments
Density
1.58 g/cc
0.0571 lb/in3
ISO 1183
Moisture Absorption at Equilibrium
1.5 %
1.5 %
50% RH; ISO 62
Water Absorption at Saturation
5.1 %
5.1 %
ISO 62
Linear Mold Shrinkage, Flow
0.0022 cm/cm
0.0022 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse
0.0060 cm/cm
0.0060 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties
Metric
English
Comments
Tensile Strength at Break
80.0 MPa
11600 psi
at yield, conditioned, 50 mm/min; ISO 527-1,-2
80.0 MPa
11600 psi
conditioned, 5 mm/min; ISO 527-1,-2
140 MPa
20300 psi
5 mm/min; ISO 527-1,-2
Elongation at Break
2.0 %
2.0 %
5 mm/min; ISO 527-1,-2
3.6 %
3.6 %
conditioned, 5 mm/min; ISO 527-1,-2
Elongation at Yield
3.5 %
3.5 %
conditioned, 50 mm/min; ISO 527-1,-2
Tensile Modulus
6.50 GPa
943 ksi
conditioned, 1 mm/min; ISO 527-1,-2
11.7 GPa
1700 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength
145 MPa
21000 psi
conditioned, 2 mm/min; ISO 178-A
230 MPa
33400 psi
2 mm/min; ISO 178-A
Flexural Modulus
7.50 GPa
1090 ksi
conditioned, 2 mm/min; ISO 178-A
11.0 GPa
1600 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)
<= 10.0 kJ/m2
@Temperature -30.0 °C
<= 4.76 ft-lb/in2
@Temperature -22.0 °F
ISO 180-1A
<= 10.0 kJ/m2
@Temperature -30.0 °C
<= 4.76 ft-lb/in2
@Temperature -22.0 °F
conditioned; ISO 180-1A
<= 10.0 kJ/m2
@Temperature -40.0 °C
<= 4.76 ft-lb/in2
@Temperature -40.0 °F
ISO 180-1A
<= 10.0 kJ/m2
@Temperature -40.0 °C
<= 4.76 ft-lb/in2
@Temperature -40.0 °F
conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO)
45.0 kJ/m2
21.4 ft-lb/in2
conditioned; ISO 180-1U
50.0 kJ/m2
23.8 ft-lb/in2
ISO 180-1U
Charpy Impact Unnotched
4.50 J/cm2
@Temperature -30.0 °C
21.4 ft-lb/in2
@Temperature -22.0 °F
conditioned; ISO 179-1eU
5.50 J/cm2
@Temperature 23.0 °C
26.2 ft-lb/in2
@Temperature 73.4 °F
conditioned; ISO 179-1eU
6.00 J/cm2
@Temperature 23.0 °C
28.6 ft-lb/in2
@Temperature 73.4 °F
ISO 179-1eU
6.00 J/cm2
@Temperature -30.0 °C
28.6 ft-lb/in2
@Temperature -22.0 °F
ISO 179-1eU
Charpy Impact, Notched
<= 1.00 J/cm2
@Temperature -30.0 °C
<= 4.76 ft-lb/in2
@Temperature -22.0 °F
ISO 179-1eA
<= 1.00 J/cm2
@Temperature -30.0 °C
<= 4.76 ft-lb/in2
@Temperature -22.0 °F
conditioned; ISO 179-1eA
<= 1.00 J/cm2
@Temperature -40.0 °C
<= 4.76 ft-lb/in2
@Temperature -40.0 °F
ISO 179-1eA
<= 1.00 J/cm2
@Temperature -40.0 °C
<= 4.76 ft-lb/in2
@Temperature -40.0 °F
conditioned; ISO 179-1eA
1.20 J/cm2
@Temperature 23.0 °C
5.71 ft-lb/in2
@Temperature 73.4 °F
ISO 179-1eA
1.20 J/cm2
@Temperature 23.0 °C
5.71 ft-lb/in2
@Temperature 73.4 °F
conditioned; ISO 179-1eA
Puncture Energy
5.00 J
@Temperature -30.0 °C
3.69 ft-lb
@Temperature -22.0 °F
ISO 6603-2
7.00 J
@Temperature 23.0 °C
5.16 ft-lb
@Temperature 73.4 °F
ISO 6603-2
9.00 J
@Temperature 23.0 °C
6.64 ft-lb
@Temperature 73.4 °F
conditioned; ISO 6603-2
Electrical Properties
Metric
English
Comments
Volume Resistivity
1.00e+13 ohm-cm
1.00e+13 ohm-cm
conditioned; IEC 60093
1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance
1.00e+14 ohm
1.00e+14 ohm
conditioned; IEC 60093
1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant
4.2
@Frequency 1.00e+6 Hz
4.2
@Frequency 1.00e+6 Hz
IEC 60250
4.5
@Frequency 1.00e+6 Hz
4.5
@Frequency 1.00e+6 Hz
conditioned; IEC 60250
4.7
@Frequency 100 Hz
4.7
@Frequency 100 Hz
IEC 60250
8.0
@Frequency 100 Hz
8.0
@Frequency 100 Hz
conditioned; IEC 60250
Dielectric Strength
27.0 kV/mm
686 kV/in
conditioned; IEC 60243-1
28.0 kV/mm
711 kV/in
IEC 60243-1
Dissipation Factor
0.013
@Frequency 100 Hz
0.013
@Frequency 100 Hz
IEC 60250
0.019
@Frequency 1.00e+6 Hz
0.019
@Frequency 1.00e+6 Hz
IEC 60250
0.045
@Frequency 1.00e+6 Hz
0.045
@Frequency 1.00e+6 Hz
conditioned; IEC 60250
0.13
@Frequency 100 Hz
0.13
@Frequency 100 Hz
conditioned; IEC 60250
Comparative Tracking Index
350 V
350 V
Solution A; IEC 60112
Thermal Properties
Metric
English
Comments
CTE, linear, Parallel to Flow
20.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
11.1 μin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow
90.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
50.0 μin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Melting Point
225 °C
437 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi)
220 °C
428 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)
205 °C
401 °F
ISO 75-1,-2
Deflection Temperature at 8.0 MPa
135 °C
275 °F
ISO 75-1,-2
Vicat Softening Point
>= 200 °C
>= 392 °F
50 N; 120 °C/h; ISO 306
>= 200 °C
>= 392 °F
50 N; 50 °C/h; ISO 306
Flammability, UL94
V-1
@Thickness 1.60 mm
V-1
@Thickness 0.0630 in
V-0
@Thickness 3.20 mm
V-0
@Thickness 0.126 in
Oxygen Index
32 %
32 %
Method A; ISO 4589-2
Glow Wire Test
775 °C
@Thickness 1.60 mm
1430 °F
@Thickness 0.0630 in
GWIT; IEC 60695-2-12
775 °C
@Thickness 3.00 mm
1430 °F
@Thickness 0.118 in
GWIT; IEC 60695-2-12
960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
GWFI; IEC 60695-2-12
960 °C
@Thickness 3.00 mm
1760 °F
@Thickness 0.118 in
GWFI; IEC 60695-2-12
Shrinkage
0.040 %
0.040 %
post-shrinkage, transverse, 60x60x2; 120°C; 4 h; ISO 294-4
0.12 %
0.12 %
post-shrinkage, 60x60x2; 120°C; 4 h; ISO 294-4
Processing Properties
Metric
English
Comments
Melt Temperature
250 °C
482 °F
Injection molding; ISO 294
Mold Temperature
80.0 °C
176 °F
Injection molding; ISO 294
Dry Time
2.00 - 6.00 hour
@Temperature 80.0 °C
2.00 - 6.00 hour
@Temperature 176 °F
Moisture Content
0.030 - 0.070 %
0.030 - 0.070 %
residual; Karl Fischer test
業(yè)務(wù)部:李厚佳
Email:ppslcp@163.com
http://www.shabosl.com/
Tel:18219005688:李生
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。