德國朗盛Lanxess Durethan? BKV 115 DUS008 000000 Nylon 6, 15% Glass Fiber玻璃纖維15%,注塑、修改,影響熱老化穩(wěn)定;
Information provided by LANXESS.
Categories:
Polymer; Thermoplastic; Nylon; Nylon 6; Nylon 6, 20% Glass Fiber Filled; Nylon 6, Glass Filled, Impact Grade; Nylon 6, Heat Stabilized
Material Notes:
PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilized
Add to Folder: My Folder
Physical Properties
Metric
English
Comments
Density
1.228 g/cc
0.04436 lb/in3
ISO 1183
Mechanical Properties
Metric
English
Comments
Tensile Strength at Break
65.0 MPa
9430 psi
conditioned, 5 mm/min; ISO 527-1,-2
115 MPa
16700 psi
5 mm/min; ISO 527-1,-2
Elongation at Break
4.0 %
4.0 %
5 mm/min; ISO 527-1,-2
14 %
14 %
conditioned, 5 mm/min; ISO 527-1,-2
Tensile Modulus
2.80 GPa
406 ksi
conditioned, 1 mm/min; ISO 527-1,-2
5.60 GPa
812 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength
95.0 MPa
13800 psi
conditioned, 2 mm/min; ISO 178-A
185 MPa
26800 psi
2 mm/min; ISO 178-A
Flexural Modulus
2.50 GPa
363 ksi
conditioned, 2 mm/min; ISO 178-A
4.90 GPa
711 ksi
2 mm/min; ISO 178-A
Charpy Impact Unnotched
5.00 J/cm2
@Temperature -30.0 °C
23.8 ft-lb/in2
@Temperature -22.0 °F
ISO 179-1eU
6.50 J/cm2
@Temperature 23.0 °C
30.9 ft-lb/in2
@Temperature 73.4 °F
ISO 179-1eU
8.00 J/cm2
@Temperature 23.0 °C
38.1 ft-lb/in2
@Temperature 73.4 °F
conditioned; ISO 179-1eU
Charpy Impact, Notched
<= 1.00 J/cm2
@Temperature 23.0 °C
<= 4.76 ft-lb/in2
@Temperature 73.4 °F
ISO 179-1eA
1.00 J/cm2
@Temperature -30.0 °C
4.76 ft-lb/in2
@Temperature -22.0 °F
ISO 179-1eA
Thermal Properties
Metric
English
Comments
Melting Point
220 °C
428 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi)
215 °C
419 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)
195 °C
383 °F
ISO 75-1,-2
Processing Properties
Metric
English
Comments
Melt Temperature
280 °C
536 °F
Injection molding; ISO 294
Mold Temperature
80.0 °C
176 °F
Injection molding; ISO 294
Dry Time
2.00 - 6.00 hour
@Temperature 80.0 °C
2.00 - 6.00 hour
@Temperature 176 °F
Moisture Content
0.030 - 0.12 %
0.030 - 0.12 %