| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 其它性能 | 熔體流動速率 | ASTM D-1238 | 5.0 | g/10min | ||
| 基本性能 | 24小時吸水率 | ASTM D-570 | 3 | % | ||
| 物理性能 | 泰伯磨耗量 | H 18輪 | ASTM D-1044 | 90 | mg/1000rev | |
| 泰伯磨耗量 | CS-17輪 | ASTM D-1044 | 2 | mg/1000rev | ||
| 比重 | ASTM D-792 | 1.07 | ||||
| 機械性能 | 硬度計硬度 | ASTM D-2240 | 30 | |||
| 揉曲模量 | 23℃ | ASTM D-790 | 28. | Mpa | ||
| 埃佐沖擊強度 | 23℃ | ASTM D-256 | 不破裂 | J/m | ||
| 斷裂拉伸力 | ASTM D-638 | 26.2 | Mpa | |||
| 初耐撕裂性能 | ASTM D-1004 | 77 | kn/m | |||
| 斷裂伸長 | ASTM D-638 | 700 | % | |||
| 電氣性能 | 拉伸力 | 5%伸長 | ASTM D-638 | 1.3 | Mpa | |
| 10%伸長 | ASTM D-638 | 2.1 | Mpa | |||
| 熱性能 | 熔點 | ASTM D-3418 | 170 | ℃ | ||
| 熱畸變溫度 | @0.5Mpa | ASTM D-638 | 46 | ℃ | ||
| 維卡軟化點 | ASTM D-1525 | 83 | ℃ | |||
| 熱畸變溫度 | @0.18Mpa | ASTM D-638 | N/A | ℃ | ||
| 其它性能 | 耐揉曲切口增長性能 | ASTM D-1052 | >1×106 | |||